ZR680 ( Accurate & White )
PHYSICAL CHARACTERISTICS( LIQUID STATE ) |
AppearanceWhite liquid Density1.10 g/cm³@25℃ Viscosity450 CPS@25℃ Dp≥0.16 mm Ec8.5 mJ/cm² |
MOLDING PERFORMANCE A MOLDING PERFORMANCE @355nm point laser@330mW power@5.0m/s scanning@No UV post-cure |
Bending Modulus1500~1700 MPa Bending Strength55~60 MPa Notched Impact Strength60~68 J/m 1.2mm Bend Angle140~170° |
MOLDING PERFORMANCE B MOLDING PERFORMANCE @90min UV post-cure |
Bending Modulus2688~2790 MPa Bending Strength66~73 MPa Notched Impact Strength60~68 J/m Hardness88 Elongation at break10~15% HDT Tg CTE |
ZR710 ( Tough & White )
PHYSICAL CHARACTERISTICS( LIQUID STATE ) |
AppearanceWhite liquid Density1.10 g/cm³@25℃ Viscosity400 CPS@25℃ Dp≥0.16 mm Ec7.9 mJ/cm² |
MOLDING PERFORMANCE A MOLDING PERFORMANCE @355nm point laser@330mW power@5.0m/s scanning@No UV post-cure |
Bending Modulus2000~2300 MPa Bending Strength75~85 MPa Notched Impact Strength35~45 J/m 1.2mm Bend Angle≥170~180° |
MOLDING PERFORMANCE B MOLDING PERFORMANCE @90min UV post-cure |
Bending Modulus2813~3520 MPa Bending Strength83~90 MPa Notched Impact Strength42~50 J/m Hardness87~92 Elongation at break13~20% HDT Tg CTE |
ZR820 ( High Transparency )
PHYSICAL CHARACTERISTICS( LIQUID STATE ) |
AppearanceTransparent liquidPale Purple Density1.10 g/cm³@25℃ Viscosity190 CPS@25℃ Dp≥0.18 mm Ec6.9 mJ/cm² |
MOLDING PERFORMANCE A MOLDING PERFORMANCE @355nm point laser@150mW power@5.0m/s scanning@No UV post-cure |
AppearanceHigh Transparency Transmittance85%(MAX) Bending Modulus1500~1700 MPa Bending Strength45~55 MPa Notched Impact Strength25~35 J/m 1.2mm Bend Angle140~170° |
MOLDING PERFORMANCE B MOLDING PERFORMANCE @90min UV post-cure |
Bending Modulus1890~2340 MPa Bending Strength55~62 MPa Notched Impact Strength40~55 J/m Hardness79 Elongation at break10~15% HDT Tg CTE |
Real ABS ( ABS Like )
PHYSICAL CHARACTERISTICS( LIQUID STATE ) |
AppearanceBright yellow liquid Density1.10 g/cm³@25℃ Viscosity400 CPS@25℃ Dp≥0.16 mm Ec7.9 mJ/cm² |
MOLDING PERFORMANCE A MOLDING PERFORMANCE @355nm point laser@330mW power@5.0m/s scanning@No UV post-cure |
Bending Modulus2000~2300 MPa Bending Strength75~85 MPa Notched Impact Strength35~45 J/m 1.2mm Bend Angle≥170~180° |
MOLDING PERFORMANCE B MOLDING PERFORMANCE @90min UV post-cure |
Bending Modulus2813~3520 MPa Bending Strength83~90 MPa Notched Impact Strength42~50 J/m Hardness87~92 Elongation at break13~20% HDT Tg CTE |
Red Wood ( Tooling Board Like )
PHYSICAL CHARACTERISTICS( LIQUID STATE ) |
AppearanceEpoxy Tooling Board Like (Pink) liquid Density1.10 g/cm³@25℃ Viscosity400 CPS@25℃ Dp≥0.16 mm Ec7.9 mJ/cm² |
MOLDING PERFORMANCE A MOLDING PERFORMANCE @355nm point laser@330mW power@5.0m/s scanning@No UV post-cure |
Bending Modulus2000~2300 MPa Bending Strength75~85 MPa Notched Impact Strength35~45 J/m 1.2mm Bend Angle≥170~180° |
MOLDING PERFORMANCE B MOLDING PERFORMANCE @90min UV post-cure |
Bending Modulus2813~3520 MPa Bending Strength83~90 MPa Notched Impact Strength42~50 J/m Hardness87~92 Elongation at break13~20% HDT Tg CTE |